| Catalog Number |
ACMA00045174 |
| Description |
High Tear Strength Fluorosilicone Rubber Compound FS-R8300 is translucent uncatalyzed fluorosilicone rubber base mixed evenly with some kinds of fillers and additives. Its tear strength is higher than normal fluorosilicone rubber compound. |
| Appearance |
Translucent, smooth surface, no visible impurities |
| Application |
Used as sealing materials to resist petroleum oil, lubricant oil, hydraulic oil, transformer oil, and non-polar chemical reagents in low temperature and/or high temperature environments.
Used to produce molded, extruded, and calendered fluorosilicone parts, such as O-rings, gaskets, sealing rings, oil seals, sealing strips, sensor materials, diaphragms, membranes, and clips for fluorosilicone gaskets and pipes. |
| Shelf Life |
1 year |
| Storage |
Transported as non-dangerous substance.
Keep it in good condition of packing during transportation.
The product should be stored in a dry and ventilate place at room temperature.
Avoid from acid, alkali chemical materials and other impurities. |
|
Appendix
| High Tear Strength Fluorosilicone Rubber Compound FS-R8300 |
|---|
| Items | Testing Method | FS-R8330 | FS-R8340 | FS-R8360 | FS-R8380 | | Specific Gravity(g/cm3, 25℃) | ASTM D792 | 1.42 | 1.43 | 1.48 | 1.50 | | Hardness(Shore A) | ASTM D2240 | 30 | 40 | 60 | 80 | | Tensile Strength(MPa) Die C | ASTM D412 | 9.5 | 11.0 | 10.5 | 9.0 | | Elongation at Break(%) Die C | ASTM D412 | 350 | 400 | 350 | 250 | | Tear Strength(KN/m) Die B | ASTM D624 | 40 | 45 | 42 | 30 | | Compression Set (177℃X22hr) (25%) B type | ASTM D395 | 14 | 12 | 14 | 16 | | Volume Change(reference fuel B)(%)(23℃x70hr) | ASTM D471 | 22 | 21 | 20 | 20 |
|
| Feature |
High tear strength
Easily pigmented
Integrated advantages of both silicone rubber and fluororubber
Wide working temperature range(-60°C-200°C)
Good resistance to solvent & fuel oil
High tensile force retention at high temperature which is like silicone rubber
High insulation
High selective permeability
Meet requirements of environment protection |
| Notes |
Properties obtained using 0.6-0.8 phr 2,5-bis (tert-butylperoxy)-2,5-dimethyl hexane (DHBP). Molded 15min at 170℃, post-cured 4hr at 200℃. If other cure temperature needed, vulcanization system shall be changed. |
| Packaging |
It is available in 12.5 Kg per plastic bag and 2 bags in 1 carton. |
| Type |
High Tear Strength |