Catalog Number | ACMA00038765 |
Density | 1.83 g/cc |
Compressive Property | Compressive Yield Strength: 15.2 Mpa |
Deflection Temperature | 89 °C at 0.46 MPa (66 psi); 88 °C @Thickness 3.20 mm,unannealed; 50 °C at 1.8 MPa (264 psi); 52 °C @Thickness 3.20 mm,unannealed; |
Elongation At Break | Elongation at Yield:78 %,5 mm/min; ISO 527; 53 %,Type I, 5 mm/min; ASTM D 638 |
Flexural Modulus | 1.21 GPa,1.3 mm/min, 50 mm span; ASTM D 790; 1.28 GPa,2 mm/min; ISO 178 |
Flexural Strength | 24.0 Mpa |
Impact Test | 26.0 J @Temperature 23.0 °C |
Izod Impact-Notched | 6.15 J/cm @Temperature 23.0 °C |
Izod Impact-Unnotched | 13.4 J/cm @Temperature 23.0 °C |
Mould Shrinkage | Linear Mold Shrinkage, 0.00 % @Time 86400 sec, 50% RH; |
Specific Gravity | 1.84 g/cc |
Tensile Modulus | 1.51 GPa,1 mm/min; ISO 527; 1.70 GPa,5 mm/min; ASTM D 638 |
Tensile Strength | 22.0 MPa,5 mm/min; ISO 527; 21.0 MPa,Type I, 5 mm/min; ASTM D 638 |