Catalog Number | ACMA00038764 |
Density | 1.80 g/cc |
Compressive Property | Compressive Yield Strength: 15.2 Mpa |
Deflection Temperature | 239 °C at 0.46 MPa (66 psi); 251 °C @Thickness 3.20 mm,unannealed; 160 °C at 1.8 MPa (264 psi); 198 °C @Thickness 3.20 mm,unannealed; |
Elongation At Break | 6.2 %,5 mm/min; ISO 527; 6.5 %,Type I, 5 mm/min; ASTM D 638 |
Flexural Modulus | 4.76 Gpa,1.3 mm/min, 50 mm span; ASTM D 790; 4.98 Gpa,2 mm/min; ISO 178 |
Flexural Strength | 89.0 Mpa |
Impact Test | 8.00 J,Multiaxial Impact; ISO 6603; 20.0 J @Temperature 23.0 °C Instrumented Impact Total Energy; ASTM D 3763 |
Izod Impact-Notched | 4.88 J/cm @Temperature 23.0 °C |
Izod Impact-Unnotched | 13.4 J/cm @Temperature 23.0 °C |
Mould Shrinkage | Linear Mold Shrinkage, 0.0060 - 0.0080 cm/cm @Time 86400 sec,Flow; 0.010 - 0.030 cm/cm @Time 86400 sec,Transverse |
Specific Gravity | 1.80 g/cc |
Tensile Modulus | 5.00 GPa,1 mm/min; ISO 527; 6.44 GPa,5 mm/min; ASTM D 638 |
Tensile Strength | 67.0 Mpa,5 mm/min; ISO 527; 69.0 MPa,Type I, 5 mm/min; ASTM D 638 |
Water Absorption | Moisture Absorption at Equilibrium: 0.010 %,23°C / 50% RH; ISO 62; 0.00 % @Time 86400 sec,50% RH; ASTM D 570 |
If you have any other questions or need other size, please get a quote.