Glass fibre is used as a PTFE filler as it offers much improved compression and wear properties. The material may also be inert gas sintered to further improve creep properties and reduce porosity and gas permeability (there would be a consequent loss of tensile properties). |
| Compressive Property |
Compressive Strength 1% Deformation, >9 Mpa;
Compressive Modulus, 758 Mpa |
| Elongation At Break |
>180% |
| Flexural Modulus |
1310 Mpa |
| Flexural Strength |
13.4 Mpa |
| Hardness |
Shore D 60 |
| Linear Thermal Expansion Coefficient |
Coefficient of Linear Thermal Expansion, 7.7-11.2 x10-5°C (100°C) |
| Size |
5mm diameter to 1000mm diameter |
| Specific Gravity |
2.23 - 2.26 g/cm3 |
| Tensile Strength |
31 MPa (4600 PSI) |
| Thermal Conductivity |
10.6 x 10-4 cal/cm-sec-°C |